Weicon Rust Protection 2000 Charcoal Spray

11.95 Excl. VAT

Rust Protection 2000 PLUS is used wherever metal constructions and installations, which are exposed to extreme ambient and weathering conditions, have to be protected with a longlasting and optically attractive layer.

SKU: 10021353 Category: Tags: , ,

Description

WEICON Rust Protection 2000 Plus charcoal-grey, 400 ml

Rust Protection 2000 PLUS is a particularly corrosion and weather resistant surface coating on the basis of ferric oxide (hematite). Due to the use of highly pure ferric oxide pigments in a flaky arrangement, a permanent, water and weather resistant protection of the surface is achieved. Rust Protection 2000 PLUS is used wherever metal constructions and installations, which are exposed to extreme ambient and weathering conditions, have to be protected with a longlasting and optically attractive layer .

Applications
– Hall and steel constructions
– Iron railings, lattice towers
– Fences, handrails and balcony railings
– Movable gates and outdoor lamps
– Renovation of intact lacquer coatings and all parts with high corrosion risk, e.g. welding seams, threads, edges, screws and nuts.

Item features
– Colour: charcoal-grey / DB 703
– Application: Indoors and outdoors
– Binding agent: Acrylic resin
– Pigment: Lamellar hematite
– Pigment purity: > 90% ferric oxide
– Percentage of metal in dry film: about. 58 %
– Content: 400 ml
– Specific weight: 1,3 – 1,4 g/cm³
– Recommended primer: not necessary
– Processing temperature: +5 to +35, optimum temperature from +18 to + 25 °C
– Consumption at 1.5 cross coats: about. 160 ml/m²
– Layer thickness at 1.5 cross coats: about. 60-80 µm
– dust dry after: about. 30 Min.
– Hardened after: about. 24 h
– paintable: about. 24 h
– Abrasion-resistant: abrasion-resistant
– Cross cutting DIN 53151 / ISO 2409: Cross cut characteristic value GT 0 to GT 1
– Salt spraying test DIN 50021 / DIN 53167: >2.000 h
– Mandrel bend test DIN EN ISO 1519 no hair cracking
– Top coating: not required
– Temperature resistance after complete hardening: about -50 to +300 °C
– Storage stability: 24 months